Pop Goes the Slip! Charlie and Linda Riggs’ Naked Raku Technique

Posted By Charlie and Linda Riggs On February 10, 2014 @ 9:13 am In Daily,Features,Raku | 2 Comments

620_featNaked raku gets its racy name because during the process of firing, the outer shell of slip that was applied falls off revealing the “naked” surface of the pot underneath. Charlie and Linda Riggs get some beautiful results from this technique. Today, in an excerpt from our free download Successful Tips and Techniques for Raku Firing: How to Select Raku Clays, Glazes, Kilns and Combustibles, Charlie and Linda share their technique.


 

Naked raku gets its racy name because during the process of firing, the outer shell of slip that was applied falls off and the surface of the pot returns to the original clay exterior. The pot is then “naked,” without a covering of glaze, whereas in a standard raku firing, a potter applies glaze to the pot and fires it to the desired temperature. The glaze matures on the pot and becomes part of the pot as a decorative surface.

 


 

For more on naked raku firing, check out Naked Raku and Related Bare Clay Techniques, which is available in the Ceramic Arts Daily Bookstore.

Order your copy today!

 

 


 

Like Dry Cracked Mud

 

We use a method of naked raku that employs a very thick slip that is applied to the surface of a pot. When it dries, it shrinks and crackles like mud does on the side of a road. The vessel is fired to 1450°F, then carefully removed from the kiln and placed into a metal can lined with newspaper. Then the can is sealed with a tight-fitting lid. This infuses the pot with smoke. The thick slip resists the smoke so that the pot surface remains white underneath it. The crackles in the slip allow the smoke to reach the surface of the pot. When the pot is finished and the slip is removed, you have a pot with a beautiful black crackle surface.

click to enlarge

click to enlarge

 

This technique requires persistence and patience. It takes practice to remove the pot from the kiln without knocking off the slip. The slip itself requires slight adjustments to the amount of alumina. It is also important to use the right type of fire clay in your slip. To find a slip that works for us, we bought samples of all of the types of fire clay we could find that were easily available across the country. We found one that worked very well, Hawthorne, but then later, through serendipity, made a batch with Lincoln fire clay and it stayed on the pot even more reliably during the raku process. The final recipe we arrived at is measured by volume: 5 parts Lincoln fire clay, 3 parts EPK kaolin, and 2 parts alumina hydrate. Mix this up with water into a thick slip.

 

The Process

 

Mix the dry ingredients with water until you get a consistency of thick cake batter (figure 1). Add more alumina hydrate if the slip doesn’t stick well to the pot during the raku process and subtract it from the recipe if the slip is difficult to remove from the surface after firing.

 

click to enlarge

click to enlarge

Mask off the areas you want to remain black using house painter’s tape (figure 2). This tape is less sticky than regular masking tape and is less likely to harm the surface of your pot.

 

To get a pot with uniform crackles, lower it down into the slip and remove it all in one uniform movement (figure 3).

 

Carefully remove the tape, taking care not to get any slip on the areas that you want to remain black (figure 4). This slip is very sticky at this stage and is difficult to wipe off without leaving residual clay marks on the pot.

 

Immediately put the pot into your raku kiln (figure 5). This means within first 2–5 minutes after applying the slip. Don’t allow any drying at all. Fire the kiln quickly to 400–500°F and soak at that temperature until the slips loses all its moisture and begins to crackle (about 15 minutes). It will turn a dull gray and no longer have a shine on the surface. Then fire the pot up to 1450°F.

 

While the pot is in the kiln, line a steel can that is slightly larger than the pot with a several sheets of newspaper (figure 6). This size of container lessens the air space during the smoking process, which will force more carbon/smoke into the slip crackles on the pot.

click to enlarge

click to enlarge

 

At 1450°F (figure 7), use raku tongs to quickly and carefully remove the pot and place it in the metal can reduction chamber that’s been prepared for it. Place some newspaper on top of the pot before closing the can. This enhances the blackening of the piece from the top down.

 

click to enlarge

click to enlarge

Allow it to cool in the can for about 10 minutes. Open the lid, allow the smoke to clear, and look in. The slip will be black (figure 8). Wearing raku/welders gloves, lift the pot out. Note: The piece may still be very hot, so use caution when handling it, even when wearing gloves. Place it on a kiln shelf, fire brick, or other non-flammable surface to cool. The slip will either fall off as you remove it from the can or you will need to wait until it cools so you can gently remove the slip using your fingers (figure 9). Remove excess slip and dust from the pot with a plastic scraper, or an old credit card (figure 10). Rub the rest of the dust off with a terry cloth towel. The cleaned pot is ready to seal with wax or an acrylic sealant.

click to enlarge

click to enlarge

 

Linda and Charlie Riggs are featured in Naked Raku and Related Bare Clay Techniques book by Eduardo Lazo. Visit ceramicartsdaily.org/bookstore for more information.

click to enlarge

click to enlarge

 


 

For more great alternative firing techniques, be sure to download your free copy of Successful Tips and Techniques for Raku Firing: How to Select Raku Clays, Glazes, Kilns and Combustibles.

 


 

 
 

Article printed from Ceramic Arts Daily: http://ceramicartsdaily.org