Gemstones in high fire ^10 RDX
Posted 12 December 2012 - 05:34 PM
I have another sorta wierd series of tests i have been screwing around with. Melting Gems!!
At this point i have run about 20 types of minerals through the high fire reduction firing, most of which act as you would expect; they melt or explode!
But a few have seriously confused me, Sodalite will off gas and change color from blue to WHITE leaving its container glazed. This could be fun in a saggar firing!!!
Obsidean, being volcanic glass, melts yielding a gorgeous blue-black glassious puddle/smeer.
The big one that has my mind totally boggled is Oregon Sunstone, which is a gem quality Plagioclase Feldspar.
I got a few little pieces for 25 cents each and run them through the fire in my normal way.
Being a feldspar i thought it would melt, or maybe turn white like other silicates i have tried (quartz, sodalite, agate etc).
To my surprise, it did neither of these things!!!!
They did not blow up, nor crack, but they did change color from a semi transparent yellow to almost a perfect clear!
I talked to a gem hound friend of mine and apparently a lot of rubys and diamonds are "heat treated" to help clarify them before they are cut and sold. Wierd!
Well anyway, thought some of ya'll might think this interesting.
Posted 03 January 2013 - 06:18 PM
The obsidian would be pretty to see. One thing you might consider regarding heating these gems. a lot of them have air pockets and somewhat rare is an enhydro (small water chamber) Do you think some of these could be reasons for the exploding? If they were ground to a powder do you think they would react in other ways? Have you tried carnelian or mookait jasper? Those two are some of my favorites!!
Posted 03 January 2013 - 08:04 PM
As they are both "pretty much" just quartz (SiO2).
But you never know really!
I encourage people to experiment with this. My "standard way of firing a stone" is to toss a piece or two into a scrap pinchpot or bowl then COVER IT WITH A SCRAP SHELF OR PLATE OR BOWL OR SHARD.
Covering stone test is essential! Fast firing schedules and possible air/atmoshreric inclusions in the stone can very possibly make them blow up! If you can see a water inclusion in a stone, dont fire it! I had some quartz with carbon inclusions but i lost them before i could test them.
I always use small pieces typically no bigger than a pea; also it seems i use a lot of flakes because i will buy a big piece and then hit it with a hammer till i get some nice looking test pieces.
A friend of mine test fired a polished fluorite crystal about the size of a walnut and it BLEW UP bad............ pieces were everywhere, stuck onto glazed pieces, eaten into shelves and brick. He says he thinks it melted and spattered but i really dont think that was the case. Another important thing to note this was covered but only partially.
I am a Geology student and therefore i have good reference books into chemical compositions, i avoid anything with Chlorine, chemical water and also high refractory minerals (like kyanite) because i already know what they are going to do more or less.
Some of my favorite tests have been granites; all the different light and dark colored minerals included in the visible matrix melts differently. Find granite with very large grain sizes and some with small sizes and look at the difference. Or try some basalt, which, chemically is basically the same except the minerals in it have not seperated from each other in the matrix.
Posted 22 February 2013 - 08:20 PM
i am new to this posting, and new to pottery, but I am also a rock collector and had been wondering about the effects of gemstones in firing. Nice to know not to try it, I do not want explosions. I have all the stones you talked about and many more, kinda went a little overboard. But do you put pieces in your finished pieces? How would you attach them and how do you make the setting considering shrinking.
Posted 25 February 2013 - 12:47 AM