Greetings; I am completely new to ceramic tech...I have designed a line of products that I origionally intended to produce in plastics, I am now considering using fired ceramics instead. This line of products are basically figurines that would be roto or slush cast...because of the complexity and many under cuts constructing hard molds with drafts etc would prove difficult so I would like to use a flexable rubber mold but these are not able to draw out moisture so my question is this...Is there a product that is self setting similar to plaster of paris that can then be fired into a ceramic like porcelin or stone ware?
Share Topic:
Page 1 of 1
roto cast
materials
Rate Topic:
MultiQuote
#2
Laura A Strike 
- Member
-
- Group: Members
- Posts: 19
- Joined: 07-February 11
- LocationIrving,Texas
Posted 29 February 2012 - 10:35 AM
I do not understand the problem.
Normally you would make a copy of your product and then create a plaster mold in sections. The number of sections woud be determined by the complexity of the form. After the plaster is set and dry, clay slip can be poured into the mold.
You need to make sure to drain the excess slip after set up. Addition pieces can be slipped in place after removed from mold.
You cannot fire extremely thick clay, it is likely to explode.
Show examples of your product for more ideas.
Normally you would make a copy of your product and then create a plaster mold in sections. The number of sections woud be determined by the complexity of the form. After the plaster is set and dry, clay slip can be poured into the mold.
You need to make sure to drain the excess slip after set up. Addition pieces can be slipped in place after removed from mold.
You cannot fire extremely thick clay, it is likely to explode.
Show examples of your product for more ideas.
#3
Chris Campbell
- Advanced Member
-
- Group: Members
- Posts: 1,365
- Joined: 07-April 10
- LocationRaleigh, NC
Posted 29 February 2012 - 10:55 AM
"Is there a product that is self setting similar to plaster of paris that can then be fired into a ceramic like porcelin or stone ware?"
I have never heard of one. I make molds from castable materials that can be fired but the resulting mold is not smooth enough to contain a finished product. There are mold making consulting services that might be able to help you. I don't think you will be able to get away from multiple part molds if you have so many undercuts.
I have never heard of one. I make molds from castable materials that can be fired but the resulting mold is not smooth enough to contain a finished product. There are mold making consulting services that might be able to help you. I don't think you will be able to get away from multiple part molds if you have so many undercuts.
Chris Campbell
Contemporary Fine Colored Porcelain
www.ccpottery.com
"My Artwork would not exist without a thriving global pottery community.
In the isolation of a studio, an artist can begin to feel like an island, but in truth
we are all part of archipelagoes; chains of islands loosely connected by a stream
of information that enhances our Artwork.”
Contemporary Fine Colored Porcelain
www.ccpottery.com
"My Artwork would not exist without a thriving global pottery community.
In the isolation of a studio, an artist can begin to feel like an island, but in truth
we are all part of archipelagoes; chains of islands loosely connected by a stream
of information that enhances our Artwork.”
#4
Matt Oz
- Advanced Procrastinator
-
- Group: Members
- Posts: 201
- Joined: 16-December 11
Posted 29 February 2012 - 04:48 PM
I know what your asking and have never heard of anything either, if there is, I would imagine the fumes would be pretty toxic during firing.
I think the closest your going to get is a cold cast porcelain resin, which you probably already know about.
I think the closest your going to get is a cold cast porcelain resin, which you probably already know about.
#5
Lucille Oka
- Advanced Member
-
- Group: Members
- Posts: 756
- Joined: 02-July 10
Posted 29 February 2012 - 11:38 PM
Yes there is. It is used in metal casting specially lost wax casting. It is called 'investment' but you must research the materials and specifics to see if it is what you are looking for. However investment is not meant for permanency.
INRI